Pergunta
1.The cylinder is made of casting, and the cylinder must undergo aging treatment after leaving the factory, so that the internal stress generated by the cylinder during the casting process is completely eliminated. If the aging time is short, the machined cylinder will be deformed in the subsequent operation.
2. Além da carga estática, como a diferença de pressão do gás dentro e fora do cilindro e o peso das várias peças instaladas no cilindro, também carrega a força de reação na parte estática quando o vapor de ânsato é um régua e o que é um »}}}) e os rigorosos e as várias forças»), o »}) e a flaginagem e os vários lagos (}}}) e a flaginagem (}}}) e a flaginagem e a interação}
3.The load of the cylinder increases or decreases too quickly, especially when the temperature changes rapidly during rapid start-up, shutdown and working condition changes, the method of warming up the cylinder is incorrect, and the insulation layer is opened too early during shutdown and maintenance, etc. Large thermal stress and thermal deformation.
4. O estresse é gerado no cilindro durante a usinagem ou após a soldagem de reparo, mas o cilindro não é temperado para eliminá -lo, resultando em grande estresse residual no cilindro e deformação permanente durante a operação .
5.In the process of installation or maintenance, due to the maintenance process and maintenance technology, the expansion gap of the inner cylinder, the cylinder diaphragm, the diaphragm sleeve and the steam seal sleeve is not suitable, or the expansion gap of the hanging lug pressure plate is not suitable. A huge expansion force is generated to deform the cilindro .
6. A qualidade do selante do cilindro usada não é boa, há muitas impurezas ou o tipo errado; Se houver partículas estranhas difíceis no selante do cilindro, será difícil para a superfície de vedação ser fortemente combinada .
7.The tightening force of the cylinder bolts is insufficient or the material of the bolts is not qualified. The tightness of the cylinder joint surface is mainly achieved by the tightening force of the bolts. The thermal stress and high temperature generated when the unit starts and stops or increases or decreases the load will cause the stress relaxation of the bolts. If the stress is insufficient, the preloading force of the bolts will gradually decrease. If the bolt material of the cylinder is not good, the bolt will be elongated under the action of thermal stress and cylinder expansion force during long-term operation, plastic deformation or fracture will occur, the tightening force will be insufficient, and the cylinder will vazamento .
8.The cylinder bolts are tightened in the incorrect order. Generally, the cylinder bolts are tightened from the middle to both sides at the same time, that is, from the place where the vertical arc is the largest or the place where the force and deformation are the largest, so that the gap at the place with the largest deformation will be adjusted to the freedom of the front and rear of the O cilindro . transferência final e, finalmente, a lacuna desaparece gradualmente . se estiver apertada de ambos os lados para o meio, a lacuna será concentrada no meio e a superfície articular do cilindro formará uma lacuna em forma de arco, causando vazamento de vapor .}
Razão
1. O vazamento interno e externo do cilindro é geralmente causado pela instalação excêntrica da haste do pistão, o suprimento insuficiente de óleo lubrificante, o desgaste ou dano do anel de vedação e o anel de vedação, o centeno do cilindro e a scar na haste do pistão.}, portanto,, portanto, quando o cilindro na haste do pistão.}}, portanto, quando reajustado para garantir a coaxialidade da haste do pistão e do cilindro; É necessário verificar se o lubrificador trabalha de maneira confiável para garantir que os atuadores sejam bem lubrificados; Quando os anéis e os anéis de vedação são usados ou danificados, eles devem ser substituídos no tempo; Se houver impurezas no cilindro, elas devem ser removidas no tempo; Se houver cicatrizes na haste do pistão, elas devem ser substituídas .
2. Força de saída insuficiente do cilindro e ação instável são geralmente causadas pelo pistão preso ou haste do pistão, lubrificação de baixa Verifique se o lubrificador funciona de maneira confiável; Se a linha de suprimento de ar está bloqueada . quando houver água condensada e impurezas no cilindro, ela deve ser removida no tempo .
3. O efeito buffer do cilindro não é bom, o que geralmente é causado pelo desgaste do anel de vedação tampão ou pelo dano do parafuso de ajuste . neste momento, o anel de vedação e o parafuso de ajuste devem ser substituídos .}
4. O dano à haste do pistão e na cabeça do cilindro do cilindro é geralmente causado pela instalação excêntrica da haste do pistão ou pela ineficácia do mecanismo tampão . a esse respeito, a posição central da haste do pistão deve ser ajustada; O anel de vedação de buffer ou parafuso de ajuste deve ser substituído .
solução
1. Para a superfície articular, com grande deformação do cilindro ou vazamento grave de vapor, o método de moagem e raspar a superfície da junta é adotado .
If the deformation of the joint surface of the upper cylinder is within the range of 0.05mm, the joint surface of the upper cylinder shall be used as the reference surface, and the joint surface of the lower cylinder shall be painted with red dan or embossed blue paper, and the lower cylinder shall be ground and scraped according to the traces. If the deformation of the joint surface of the upper cylinder is Grande, aplique o elixir vermelho no cilindro superior, use uma régua plana grande para moer traços e moer o cilindro superior para o nível .} ou pegar o método de usinagem para nivelar a superfície da junta do cilindro superior e depois moer e raspar a superfície da junta do cilindro inferior com base no cilindro superior. Geralmente, existem dois métodos para moer e raspar a superfície articular do cilindro:
⑴ It is a bolt that does not tighten the joint surface. Use a jack to slightly push the upper cylinder to move back and forth, and grind and scrape according to the coloring of the red dan on the joint surface of the lower cylinder. This method is suitable for high-pressure cylinders with strong structural rigidity.
(2) It is the bolt that tightens the joint surface. Check the tightness of the joint surface according to the feeler gauge, measure the value and the traces pressed out, and repair and scrape the joint surface. This method can eliminate the influence of the vertical arc of the cylinder on the gap.
2. Use o material de vedação do cilindro adequado
Como não existe um padrão nacional unificado e o padrão da indústria para selante de cilindro de turbina a vapor, as matérias -primas e formulações também são diferentes e a qualidade do produto é desigual; Fabricante regular garantido para garantir o aperto do cilindro após a revisão .
3. O método de soldagem de reparo local
Since the joint surface of the cylinder is scoured by steam or corroded to form groove marks, select appropriate electrodes to level the groove marks, use a flat plate or a ruler to grind out the marks, and scrape the weld bead and the joint surface in the same plane. When the deformation of the joint surface of the cylinder is large or the steam leakage is serious, repair and weld one or two 10-20 mm fitas de vedação larga na superfície articular do cilindro inferior para eliminar a lacuna e, em seguida, meça com uma régua plana ou prenda o cilindro superior e aplique o vermelho para moer ., até que o gap seja eliminado . o processo de execução, também é muito simples. A desdobramento ou a soldagem do salto à temperatura ambiente . use eletrodos austeníticos, como A407 e A412, e cubra com pano de amianto para manter quente e fresco após a soldagem . após a temperatura ambiente, polir e raspar .}
4. revestimento ou pulverização da superfície da junta do cilindro
When there is a large area of steam leakage on the joint surface of the cylinder and the gap is about 0.50mm, in order to reduce the workload of grinding and scraping, the coating process can be used. Use the cylinder as the anode and the applicator as the cathode, and repeatedly brush the electrolytic solution on the joint surface of the cylinder. The thickness of the coating depends on the size of the gap between the joint surfaces of the cylinder. Process depends. Spraying is to use a special high-temperature flame spray gun to heat the metal powder to melt or reach a plastic state and spray it on the surface of the treated cylinder to form a coating method with the required properties. Its characteristics are simple equipment, easy operação, revestimento firme e a temperatura do cilindro após a pulverização é de apenas 70 graus -80, que não causará deformação do cilindro, e pode obter o solo resistente ao aquecimento, que deve ser resistente a spraying e a superfície e a superfície do cilindro deve ser o polido e o que deve ser o que a superfície e o cilindro deve ser o que a superfície e a superfície do cilindro deve ser o que o cilindro deve ser o que a superfície e a superfície do cilindro deve ser o que o cilindro é o que a superfície e o cilindro deve ser o que a superfície e a superfície do cilindro deve ser o que a superfície e o que é ribeirinho e a superfície do cilindro. e raspado após o revestimento e pulverização para garantir o aperto da superfície da articulação.
5. o método de preencher a superfície da junta
If the local gap leakage of the joint surface is not very large, the hardness of the 80-100 mesh copper mesh can be reduced by heat treatment, then cut into an appropriate shape, laid on the leakage of the joint surface, and then equipped with a cylinder sealant. If the gap of the joint surface is large and the leakage is serious, a groove with a width of 50mm and a depth of 5mm can be Aberto nas superfícies da articulação superior e inferior, e uma almofada dentada de IGR18ni9Ti é incorporada no meio ., pode ser ajustada com lavadoras de aço inoxidável da mesma forma .
6. métodos de controle da tensão do parafuso
If the deformation of the joint surface of the cylinder is small and uniform, new bolts can be replaced at the gaps, or the pre-tightening force of the bolts can be appropriately increased. Tighten from the middle to both sides at the same time, that is, tighten the bolts from the place with the largest vertical arc or the place with the largest stress and deformation. In theory, the pre-tightening A força do parafuso de controle pode ser calculada pela fórmula D/L menor ou igual a A, mas como os métodos de dados e medição desse cálculo ainda estão em estudo, eles não foram promovidos e estão principalmente dentro do estresse máximo permitido do parafuso de acordo com a experiência .
7. métodos de material de polímero adotados na nova era
With the further development of technology, polymer composite materials have gradually achieved successful application in cylinder maintenance. Compared with traditional methods, polymer composite materials have excellent temperature resistance, good pressure resistance, and better sealing performance, and have good plasticity. They will not be cured when heated, and the sealing film will not be In addition, it is easy to remove, and the used sealing surface can be easily wiped com etanol ou acetona absoluta sem aderir à superfície de vedação; Devido ao seu excelente desempenho, é gradualmente submetido a mais e mais empresas de cilindros são favorecidas .